C10300 Tin Plated Copper Foil
Brand Name:
OEM
Minimum Order Quantity:
50kg
Price:
Negotiable
Supply Ability:
550T Per Month
Delivery Time:
10 - 15 Days
Product Details
Highlight:
0.035mm Tin Plated Copper Foil
,C10300 Tin Plated Copper Foil
,610mm Tin Plated Copper Foil
Application:
Connector, Lead Frame Power Transistor, Electric Industrial Components
Thickness:
0.035mm- 2.5mm
Width:
7--610mm
Material:
C10300 Oxygen Free Copper
Grade:
C10300
Cu (Min):
99.95%
Alloy Or Not:
Non-alloy
Name:
Nickel Plated Copper Foil Se-Cu57 C10300
Shape:
Customised
Sample:
Avialable
Type:
Flat
Length:
Customer's Demands
Electric 20 CConductivity:
>100%IACS
State:
Custom
Package:
Fumigation Wooden Package
Standard:
JIS ASTM DIN EN ISO
Port:
SHANGHAI
Product Description
C10300 Tin Plated Copper Foil
Applications
submarine fibre optic cable, Longitudinally welded cables, Radio Frequency(RF)Cables, Copper tape screen for XLPE cable, Components for the electrical industry, Heat Sinks
Description Of Copper & Tin plating
- Copper (Cu) is used to coat zinc, aluminium, and magnesium, as first coating before further plating. It is used to improve the solderability of the named materials, decrease their electrical resistance, harden them against abrasive and adhesive wear.
- Copper plating is a phase in chromium plating of plastics. It is also used for decoration.
- Tin (Sn) is used to plate steel components already coated by nickel or copper, against corrosion; steel plates for the conservation industry; for improving the solderability of surfaces in the electronic industry. Basic and acid electrolytes are used.
| High Conductivity Copper C10300 | |||||||||
| Standard | |||||||||
| DIN | EN | ASTM | JIS | ||||||
| Material code | No. | Material code | No. | UNS No. | JIS No. | ||||
| SE-Cu 58 | 2.007 | Cu-PHC | CW020A | 10300 | C1030 | ||||
| Cu | P | ||||||||
| ≥99.95 | ≈0.003 | ||||||||
| Electrical conductivity IACS%(20℃) | 100 | Thermal conductivity W/(m*K) | 390 | ||||||
| Modulus of elasticity (KN/mm2) | 127 | ||||||||
| Merit | |||||||||
| With high purity,excellent thermal and electrical conductivity, great machinability, solder ability and corrosion resistance | |||||||||
| Mechanical Properties | |||||||||
| Temper Class | Temper | Tensile Strength | Yield Strength | Elongation A50 | Vickers Hardness | Bending Test | |||
| 90 degree (R/T) | |||||||||
| (Rm,Mpa) | (Rp0.2,Mpa) | (%) | (HV) | GW | BW | ||||
| R220 | O | 220-260 | 140max | 33min | 40-65 | 0 | 0 | ||
| R240 | 1/4H | 240-300 | 180min | 8min | 65-95 | 0 | 0 | ||
| R290 | H | 290-360 | 250min | 4min | 90-110 | 0 | 0 | ||
| R360 | EH | 360min | 320min | 2min | 110min | 0 | 0.5 | ||
Inventory: Thickness: 0.1-3.0mm Hardness Temper: Soft, 1/4H & H